Abstract

A SrCo_0.8Fe_0.2O₃ impregnated TiO₂ membrane (TiO₂–SrCo_0.8Fe_0.2O₃ membrane) was successfully prepared using a sol–gel method in combination with a wet impregnation process. The membrane was subjected to a single gas permeance test using oxygen (O₂) and nitrogen (N₂). The TiO₂ membrane was immersed in the SrCo_0.8Fe_0.2O₃ solution, dried and then calcined to affix SrCo_0.8Fe_0.2O₃ into the membrane. The effect of the acid/alkoxide (H⁺/Ti⁴⁺) molar ratio of the TiO₂ sol on the TiO₂ phase transformation was investigated. The optimal molar ratio was found to be 0.5, which resulted in nanoparticles with a mean size of 5.30 nm after calcination at 400 °C. The effect of calcination temperature on the phase transformation of TiO₂ and SrCo_0.8Fe_0.2O₃ was investigated by varying the calcination temperature from 300 to 500 °C. X-ray diffraction spectroscopy (XRD) and Fourier transform infrared (FTIR) analysis confirmed that a calcination temperature of 400 °C was preferable for preparing a TiO₂–SrCo_0.8Fe_0.2O₃ membrane with fully crystallized anatase and SrCo_0.8Fe_0.2O₃ phases. The results also showed that polyvinyl alcohol (PVA) and hydroxypropyl cellulose (HPC) were completely removed. Field emission scanning electron microscopy (FESEM) analysis results showed that a crack-free and relatively dense TiO₂ membrane (∼0.75 μm thickness) was created with a multiple dip-coating process and calcination at 400 °C. The gas permeation results show that the TiO₂ and TiO₂–SrCo_0.8Fe_0.2O₃ membranes exhibited high permeances. The TiO₂–SrCo_0.8Fe_0.2O₃ membrane developed provided greater O₂/N₂ selectivity compared to the TiO₂ membrane alone.