Abstract

Spinel compounds Li₄Ti_5−xAl_xO₁₂/C (x=0, 0.05) were synthesized via solid state reaction in an Ar atmosphere, and the electrochemical properties were investigated by means of electronic conductivity, cyclic voltammetry, and charge–discharge tests at different discharge voltage ranges (0–2.5 V and 1–2.5 V). The results indicated that Al³⁺ doping of the compound did not affect the spinel structure but considerably improved the initial capacity and cycling performance, implying the spinel structure of Li₄Ti₅O₁₂ was more stable when Ti⁴⁺ was substituted by Al³⁺, and Al³⁺ doping was beneficial to the reversible intercalation and deintercalation of Li⁺. Al³⁺ doping improved the reversible capacity and cycling performance effectively especially when it was discharged to 0 V.