Abstract

A new vanado-molybdate LiMg₃VMo₂O₁₂ has been synthesized, the crystal structure determined an ionic conductivity measured. The solid solution Li_2−zMg_2+zV_zMo_3−zO₁₂ was investigated and the structures of the z=0.5 and 1.0 compositions were refined by Rietveld analysis of powder X-ray (XRD) and powder neutron diffraction (ND) data. The structures were refined in the orthorhombic space group Pnma with a5.10, b10.4 and c17.6 Å, and are isostructural with the previously reported double molybdates Li₂M₂(MoO₄)₃ (M=M²⁺, z=0). The structures comprise of two unique (Li/Mg)O₆ octahedra, (Li/Mg)O₆ trigonal prisms and two unique (Mo/V)O₄ tetrahedra. A well-defined 1:3 ratio of Li⁺:Mg²⁺ is observed in octahedral chains for LiMg₃VMo₂O₁₂. Li⁺ preferentially occupies trigonal prisms and Mg²⁺ favours octahedral sheets. Excess V⁵⁺ adjacent to the octahedral sheets may indicate short-range order. Ionic conductivity measured by impedance spectroscopy (IS) and differential scanning calorimetry (DSC) measurements show the presence of a phase transition, at 500–600 °C, depending on x. A decrease in activation energy for Li⁺ ion conductivity occurs at the phase transition and the high temperature structure is a good Li⁺ ion conductor, with σ=1×10⁻³–4×10⁻² S cm⁻¹ and E_a=0.6 to 0.8 eV.

graphical Abstract

A new vanado-molybdate LiMg₃VMo₂O₁₂ has been synthesized and the crystal structure determined. Ionic conductivity measurements show the presence of a phase transition, at 500–600 °C. A large decrease in activation energy for Li⁺ ion conductivity occurs at the phase transition and the high temperature structure is a good Li⁺ ion conductor.