Abstract

Yellow/orange-emitting nitrogen-rich Ca_0.9Si₉Al₃(O,N)₁₆: Eu²⁺ phosphors were successfully prepared by solid-state reaction synthesis. The fluorescence excitation spectra of all of the nitrogen-rich Ca_0.9Si₉Al₃(O,N)₁₆: Eu²⁺ phosphor powders displayed two broad bands centered at about 300 nm and 400–475 nm. The first peak was assigned to the absorption of the host lattice and the second to the 4f⁷ → 4f⁶5d¹ absorption of the Eu²⁺ ions, its means enhanced 4f⁷ → 4f⁶5d excitation of Eu²⁺ ion. The absorption peak intensity increased upon increasing the Eu²⁺ doping amount, but only up to a Eu²⁺ concentration ratio of 0.15. The emission spectra of the prepared Ca_0.9Si₉Al₃(O,N)₁₆: Eu²⁺ phosphors all exhibited a single broad band in the 500–700 nm region, maximum emission peak observed at 591 nm. The room temperature decay times were observed τ₁ = 1.27 μs and τ₂ = 9.90 μs.

Graphical abstract

Full-size image (31K)