Nature460, 81-84 (2 July 2009) | doi:10.1038/nature08128; Received 4 February 2009; Accepted 11 May 2009; Published online 31 May 2009
Giant tunnel electroresistance for non-destructive readout of ferroelectric states
V. Garcia1,2, S. Fusil1,3, K. Bouzehouane1, S. Enouz-Vedrenne4, N. D. Mathur2, A. Barthélémy1 & M. Bibes1
Unité Mixte de Physique CNRS/Thales, 1 Av. A. Fresnel, Campus de l'Ecole Polytechnique, 91767 Palaiseau, France, and Université Paris-Sud, 91405 Orsay, France
Department of Materials Science, University of Cambridge, Cambridge CB2 3QZ, UK
Université d'Evry-Val d'Essonne, Bd. F. Mitterrand, 91025 Evry cedex, France
Thales Research & Technology, 1 Av. A. Fresnel, Campus de l'Ecole Polytechnique, 91767 Palaiseau, France
Correspondence to: M. Bibes1 Correspondence and requests for materials should be addressed to M.B. (Email: manuel.bibes@thalesgroup.com).
Ferroelectrics possess a polarization that is spontaneous, stable and electrically switchable1, and submicrometre-thick ferroelectric films are currently used as non-volatile memory elements with destructive capacitive readout2. Memories based on tunnel junctions with ultrathin ferroelectric barriers would enable non-destructive resistive readout3. However, the achievement of room-temperature polarization stability and switching at very low thickness is challenging4, 5. Here we use piezoresponse force microscopy at room temperature to show robust ferroelectricity down to 1 nm in highly strained BaTiO3 films; we also use room-temperature conductive-tip atomic force microscopy to demonstrate resistive readout of the polarization state through its influence on the tunnel current6, 7. The resulting electroresistance effect scales exponentially with ferroelectric film thickness, reaching 75,000% at 3 nm. Our approach exploits the otherwise undesirable leakage current—dominated by tunnelling at these very low thicknesses—to read the polarization state without destroying it. We demonstrate scalability down to 70 nm, corresponding to potential densities of >16 Gbit inch-2. These results pave the way towards ferroelectric memories with simplified architectures, higher densities and faster operation, and should inspire further exploration of the interplay between quantum tunnelling and ferroelectricity at the nanoscale.
75,000% at 3 nm. Our approach exploits the otherwise undesirable leakage current—dominated by tunnelling at these very low thicknesses—to read the polarization state without destroying it. We demonstrate scalability down to 70 nm, corresponding to potential densities of >16 Gbit inch-2. These results pave the way towards ferroelectric memories with simplified architectures, higher densities and faster operation, and should inspire further exploration of the interplay between quantum tunnelling and ferroelectricity at the nanoscale.