High-temperature ferromagnetism observed in facing-target reactive sputtered MnxTi1−xO2 films




W.B. Mia, E.Y. Jianga and H.L. BaiCorresponding Author Contact Information, a, E-mail The Corresponding Author






aTianjin Key Laboratory of Low Dimensional Materials Physics and Preparing Technology, Institute of Advanced Materials Physics, Faculty of Science, Tianjin University, No. 92 Weijin Road, Nankai District, Tianjin 300072, China






Received 3 August 2007; 


revised 16 March 2008; 


accepted 23 March 2008. 


Available online 24 April 2008.







Abstract


The crystal structure of reactive sputtered MnxTi1−xO2 films turns from anatase to rutile as x increases. All the films are ferromagnetic, with a Curie temperature above 340 K. Vacuum annealing enhances the ferromagnetism of the films, but O2 annealing weakens it, indicating that the ferromagnetism is related to the oxygen-vacancy defects created by Mn+2 dopants at Ti+4 cations. The average room-temperature moment per Mn decreases from 0.482 μB at x = 0.026 to 0.078 μB at x = 0.375. Meanwhile, the optical band gaps value decreases linearly from 3.35 eV at x = 0 to 1.73 eV at x = 0.375, suggesting that Mn ions substitute for Ti ions uniformly and the ferromagnetism is not from magnetic Mn oxide impurities. The high-temperature ferromagnetism makes the MnxTi1−xO2 films useful for the applications in spintronic devices.





Keywords: Compound semiconductors; Magnetic thin films; Magnetic properties; Vacancies; Optical transmission





Article Outline



1. Introduction
2. Experimental details
3. Results and discussion
4. Conclusions
Acknowledgements
References






























Acta Materialia
Volume 56, Issue 14, August 2008, Pages 3511-3515


Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev   honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2024 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок