Volume 61, Issue 14, August 2013, Pages 5414–5428





Transmission electron microscopy study of the reaction mechanisms involved in the carbothermal reduction of anatase





  • Laboratoire Science des Procédés Céramiques et de Traitements de Surface – UMR CNRS 7315, Centre Européen de la Céramique,12 rue Atlantis, 87068 Limoges, France






Abstract


The carbothermal reduction of anatase in titanium oxycarbide was studied by transmission electron microscopy (TEM). This study emphasizes that the reaction proceeds through complex solid–gas equilibria involving three main steps. During the first step, the carbon-monoxide-enriched atmosphere prevailing within the furnace provokes the direct transformation of anatase into the Magnéli phase. This transformation is accompanied by abnormal oxide grain growth showing a high number of stacking defects. The ordering tendency of such defects and their progressive increasing density lead to the final Ti3O5 compound. The second step of the reaction concerns the destabilization of Ti3O5 and carbon black in a high pCO atmosphere to form the oxycarbide. The titanium oxycarbide (TixOyCz) nucleates in the carbon black aggregates, giving rise to a first generation of defect-free faceted crystals (automorphous habit) characterized by a constant chemical composition. During the third step, Ti3O5 is missing and the primary carbide enters a maturation step characterized by carbon enrichment, attested by an increase in its cell parameter. This third step is characterized by the recrystallization phenomenon of the primary oxycarbide into the secondary one with an abrupt change in stoichiometry. The latter is characterized by rounded crystals (xenomorphous habit) bearing either a high density of dislocations or geometrical internal porosity linked to the migration of vacancies through the Kirkendall effect. Its further enrichment in carbon is assumed to be assisted by dislocation motion.


 


Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev   honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2024 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок