Volume 192, August 2012, Pages 38–46




Using in situ X-ray absorption spectroscopy to study the local structure and oxygen ion conduction mechanism in (La0.6Sr0.4)(Co0.2Fe0.8)O3−δ



  • Takanori Itoha, Corresponding author contact information, E-mail the corresponding author,

  • Masanobu Nakayamab



  • a AGC SeimiChemical Co., Ltd., 3-2-10 Chigasaki, Chigasaki City, Kanagawa 253-8585, Japan

  • b Department of Materials Science and Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya-city, Aichi 466-8555, Japan








Abstract


To study the local structure and oxygen ion conduction mechanism in (La0.6Sr0.4)(Co0.2Fe0.8)O3−δ (LSCF) as a function of the oxygen partial pressure (P(O2)), in situ the Co and Fe K-edge X-ray absorption spectroscopy (XAS) was measured at elevated temperatures of 900 and 1000 K. The reduction of the Co and Fe valence, i.e., the oxygen content (3−δ) in LSCF, followed the change of P(O2) from 1 to 10−4 atm during∼4000 s. The quantitative analysis of the X-ray absorption near edge structure (XANES) and the extended X-ray absorption fine structure (EXAFS) indicated that the Fe valence was higher than the Co valence at oxidative condition (δ≈0) in LSCF. Whereas the Co valence decreased more than the Fe valence after reduction of P(O2) at both 900 and 1000 K. From the relaxation plots of the valence and the oxygen content (3−δ) for Co and Fe after changing P(O2), we successfully determined Dchem and Ea of an oxygen ion migration around Co and Fe in LSCF. A structural model with and without oxygen vacancies and an oxygen ion conduction mechanism for LSCF are proposed based on these results.






Graphical abstract



A structural model with and without oxygen vacancies, and the oxygen ion conduction mechanism of LSCF were speculated. In other words, oxygen vacancies would form more preferentially around Co than Fe from the results of in situ XAS analysis during reduction, and oxygen ions needs to pass through at the vicinity of Fe from the results of Dchem and Ea.




Full-size image (26K)




Дизайн и программирование N-Studio 
А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я
  • Chen Wev   honorary member of ISSC science council

  • Harton Vladislav Vadim  honorary member of ISSC science council

  • Lichtenstain Alexandr Iosif  honorary member of ISSC science council

  • Novikov Dimirtii Leonid  honorary member of ISSC science council

  • Yakushev Mikhail Vasilii  honorary member of ISSC science council

  • © 2004-2024 ИХТТ УрО РАН
    беременность, мода, красота, здоровье, диеты, женский журнал, здоровье детей, здоровье ребенка, красота и здоровье, жизнь и здоровье, секреты красоты, воспитание ребенка рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок медицина, клиники и больницы, болезни, врач, лечение, доктор, наркология, спид, вич, алкоголизм православные знакомства, православный сайт творчeства, православные рассказы, плохие мысли, православные психологи рождение ребенка,пол ребенка,воспитание ребенка,ребенок дошкольного возраста, дети дошкольного возраста,грудной ребенок,обучение ребенка,родить ребенка,загадки для детей,здоровье ребенка,зачатие ребенка,второй ребенок,определение пола ребенка,будущий ребенок